Morphological Observation of the Mechanically Alloying(Bi2O3)0.80(Nb2O5)0.20
-
- TAKAI Shigeomi
- Department of Materials Science, Faculty of Engineering, Tottori University
-
- SHIRAISHI Noritake
- Department of Materials Science, Faculty of Engineering, Tottori University
-
- ATAKE Tooru
- Materials and Structures Laboratory, Tokyo Institute of Technology
-
- ESAKA Takao
- Department of Materials Science, Faculty of Engineering, Tottori University
書誌事項
- タイトル別名
-
- Morphological Observation of the Mechanically Alloying (Bi<sub>2</sub>O<sub>3</sub>)<sub>0.80</sub>(Nb<sub>2</sub>O<sub>5</sub>)<sub>0.20</sub>
この論文をさがす
抄録
<p>The mechanical alloying (MA) process of the oxide ion conductor (Bi2O3)0.80(Nb2O5)0.20 has been studied by means of X-ray diffraction, SEM observation and particle size measurements. The formation of the solid solution was supposed to proceed by flattening the sample powders into plate shapes and the repeated laminations as the case of the formation of metallic alloys. During milling, the crystallite size decreases down to 10 mm or smaller while the aggregated particle size was remaining about 1 μm.</p>
収録刊行物
-
- Electrochemistry
-
Electrochemistry 67 (5), 466-469, 1999-05-05
公益社団法人 電気化学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001277393212800
-
- NII論文ID
- 10002567191
-
- NII書誌ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
-
- NDL書誌ID
- 4725041
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可