Morphological Observation of the Mechanically Alloying (Bi<sub>2</sub>O<sub>3</sub>)<sub>0.80</sub>(Nb<sub>2</sub>O<sub>5</sub>)<sub>0.20</sub>
-
- TAKAI Shigeomi
- Department of Materials Science, Faculty of Engineering, Tottori University
-
- SHIRAISHI Noritake
- Department of Materials Science, Faculty of Engineering, Tottori University
-
- ATAKE Tooru
- Materials and Structures Laboratory, Tokyo Institute of Technology
-
- ESAKA Takao
- Department of Materials Science, Faculty of Engineering, Tottori University
Bibliographic Information
- Other Title
-
- Morphological Observation of the Mechanically Alloying(Bi2O3)0.80(Nb2O5)0.20
Search this article
Abstract
<p>The mechanical alloying (MA) process of the oxide ion conductor (Bi2O3)0.80(Nb2O5)0.20 has been studied by means of X-ray diffraction, SEM observation and particle size measurements. The formation of the solid solution was supposed to proceed by flattening the sample powders into plate shapes and the repeated laminations as the case of the formation of metallic alloys. During milling, the crystallite size decreases down to 10 mm or smaller while the aggregated particle size was remaining about 1 μm.</p>
Journal
-
- Electrochemistry
-
Electrochemistry 67 (5), 466-469, 1999-05-05
The Electrochemical Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001277393212800
-
- NII Article ID
- 10002567191
-
- NII Book ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
-
- NDL BIB ID
- 4725041
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Allowed