Kinetics of Oxygen Reduction in Molten Alkali Carbonates under Pressurized Air/CO2 0xidant Gas Conditions

DOI Web Site Web Site 参考文献32件
  • LEE Choong-Gon
    Department of Applied Chemistry, Graduate School of Engineering, Tohoku University
  • YAMADA Kohta
    Institute for Advanced Materials Processing, Tohoku University
  • HISAMITSU Yasunari
    Department of Applied Chemistry, Graduate School of Engineering, Tohoku University
  • ONO Yu
    Department of Applied Chemistry, Graduate School of Engineering, Tohoku University
  • UCHIDA Isamu
    Department of Applied Chemistry, Graduate School of Engineering, Tohoku University

書誌事項

タイトル別名
  • Kinetics of Oxygen Reduction in Molten Alkali Carbonates under Pressurized Air/CO<sub>2</sub> Oxidant Gas Conditions

この論文をさがす

抄録

<p>The electrode kinetics and mechanism of oxygen reduction at gold electrodes in (53 + 47) mol % (Li + Na)CO3, (62 + 38) mol% (Li + K)CO3 and (43.5 + 31.5 + 25) mol % (Li + Na + K)CO3 melts have been investigated under pressurized Air/CO2 oxidant gas conditions in a temperature range of 823-973 K. The total pressure was changed from 1.0 to 5.0 atm with a constant ratio of Air/CO2 = 70/30, 80/20, 90/10 or 95/5. It was observed that the oxygen reduction current in cyclic voltammograms increased with the total pressure, indicating that the concentration of reactive species increased. The analyses of the gas partial pressure dependence on Warburg coefficients, which were obtained by ac impedance measurements, revealed that the reaction process in the tested conditions was dominated by the mixed diffusion of superoxide ion O2− and dissolved CO2.</p>