凝固中に遠心力を作用させた2%Feを含むAl-11%Si合金のマクロ偏析 Macroscopic segregation in Al-11 mass%Si slloy containing 2 mass%Fe solidified under centrifugal force

この論文にアクセスする

この論文をさがす

著者

抄録

In order to reduce iron content in aluminum alloys, a technique has been tried to segregate and separate intermetallic compounds containing iron by applying centrifugal force during solidification. The castings solidified under centrifugal force have shown obvious macroscopic segregation. The iron content decreases in the inner part of cast ingot from 2.07 mass% to 0.27 mass% due to the centrifugal force and the reduction ratio of iron has reached 87%. Thus, the utilization of this segregation phenomenon is a possible way of removal of the iron in aluminum alloys.

収録刊行物

  • 軽金属  

    軽金属 48(2), 93-97, 1998-02-28 

    The Japan Institute of Light Metals

参考文献:  7件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002664453
  • NII書誌ID(NCID)
    AN00069773
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    04515994
  • NDL 記事登録ID
    4413753
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-284
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ