- Age hardening and fatigue strength of Al-Zn alloys with high Zn concentration.
- 高濃度のZnを含有するAl-Zn合金の時効硬化と疲労強度
- コウ ノウド ノ Zn オ ガンユウスル Al Zn ゴウキン ノ ジコウ コ
この論文をさがす
抄録
Soft surface layer formed after low temperature aging was studied on Al–12, 16, 18 and 20 mass%Zn alloy by means of hardness test and resistometry. The soft surface layer could not be observed in 20%Zn alloy aged at 273 K when the quenching temperature was higher than 673 K. The thickness of the soft surface layer in the specimen aged at 273 K after quenching from 673 K decreased with increase of Zn concentration. Aging curve in resistivity showed the depression of the growth of GP zones in the surface layer relative to the interior of the specimen. Fatigue strength in the repeated tensile mode was higher when the soft surface layer formed during aging was thicker. The soft surface layer formed by partial reversion treatment also increased fatigue strength.
収録刊行物
-
- 軽金属
-
軽金属 48 (2), 98-102, 1998
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206337058048
-
- NII論文ID
- 10002664461
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK1cXhsV2rsb4%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 4413754
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可