SO_4^<2->イオンを含んだ溶液中でのアルミニウム合金の孔食発生に関する電気化学的検討 Electrochemical investigation on pitting corrosion generation of aluminum alloy in the solution containing SO_4^<2-> ion

この論文にアクセスする

この論文をさがす

著者

    • 黒田 周 KURODA Shuu
    • 三菱アルミニウム(株)技術開発センター Technical development center, Mitsubishi Aluminum Co., Ltd.
    • 当摩 建 TOHMA Ken
    • 三菱アルミニウム(株)技術開発センター Technical development center, Mitsubishi Aluminum Co., Ltd.

抄録

To investigate the effect of SO<sub>4</sub><sup>2-</sup> ion on pitting corrosion behavior of aluminum and aluminum alloy brazing sheets immersion corrosion test and electrochemical measurements were carried out in the solution of lower chloride concentration containing SO<sub>4</sub><sup>2-</sup> ion. As the SO<sub>4</sub><sup>2-</sup> ion reduced the anodic and cathodic reaction rate, the pitting corrosion resistance of aluminum increased. The pitting corrosion occurred even in solution containing SO<sub>4</sub><sup>2-</sup> when the cathodic reaction was high enough. In that case the pitting corrosion rate was much higher than that in the SO<sub>4</sub><sup>2-</sup> ion free solution. Higher pitting corrosion rate induced by SO<sub>4</sub><sup>2-</sup> ion was due to the lower pitting corrosion density which was closely related with the thicker oxide film formed on aluminum surface. The probability of pitting corrosion was estimated with the relation between <i>E</i><sub>corr</sub> and <i>E</i><sub>rep</sub> value in anodic polarization measurement in the solution.

収録刊行物

  • 軽金属  

    軽金属 48(6), 282-287, 1998-06-30 

    The Japan Institute of Light Metals

参考文献:  8件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002664848
  • NII書誌ID(NCID)
    AN00069773
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    04515994
  • NDL 記事登録ID
    4512223
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-284
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ