- effect of Mg on activation of aluminum in pitting corrosion
この論文をさがす
抄録
The effect of Mg on pitting corrosion of aluminum has been studied in terms of activation, repassivation, in comparison with the effect of Zn. The pitting potential and passive current in 0.5 NaCl were slightly decreased by alloyed Mg, respectively, but the repassivation potential tended to increase. In current transients and open circuit potential measurements, preferential dissolution of Mg, causing an aluminum enrichment, was considered in 6 M HC1 (pit-like solution) . In addition, after immersion in 6 M HC1, the pitting potential increased over the value of pure Al. Therefore, it can be considered that alloyed Mg has little effect to activate aluminum at first, but that aluminum dissolution rate is reduced by an aluminum enrichment caused by the preferential dissolution of Mg in the local environment.
収録刊行物
-
- 軽金属
-
軽金属 48 (8), 385-389, 1998
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206336225536
-
- NII論文ID
- 10002665068
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK1cXlslKktrc%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 4652054
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可