- Effects of welding conditions on axial shortening behavior and tensile strength of friction welded joints of 5052 aluminum alloy
- 5052 アルミニウム ゴウキン マサツ アッセツ ツギテ ノ ヨリ キョドウ オヨビ ヒッパリ ツヨサ ニ オヨボス アッセツ ジョウケン ノ エイキョウ
この論文をさがす
抄録
5052 aluminum alloy were friction welded using a brake type friction welding machine. Effects of the welding conditions on axial shortening behavior and tensile strength of the friction welded joints were investigated. Upset pressure such as welding conditions were determined 1.0, 1.5 and 2.0 times of friction pressure. Burn-off length increased almost lineally just after the start of friction process. Forge length increases sharply immediately after the upset process, then, forge length reaches constant value. Total loss is a good correlation with burn-off length and forge length. In case of the upset pressure being equal to friction pressure, the tensile strength of welded joints veried very widely. If upset pressure is setting higher than friction pressure, tensile strength of welded joints become higher than that of the joint with friction pressure equal to upset pressure, and amount of scatter were reduced. The maximum tensile strength of welded joints shows 92% that of the base metal.
収録刊行物
-
- 軽金属
-
軽金属 48 (8), 400-404, 1998
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206336230016
-
- NII論文ID
- 10002665104
- 10004453643
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK1cXlslKkt7w%3D
-
- ISSN
- 18808018
- 04515994
- http://id.crossref.org/issn/04515994
-
- NDL書誌ID
- 4652065
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可