Al-Si合金ろう材の電気化学的性質に及ぼすCuとZn添加の影響 Effect of Cu and Zn addition on electrochemical Properties of Al-Si brazing filler

この論文にアクセスする

この論文をさがす

著者

    • 黒田 周 KURODA Shuu
    • 三菱アルミニウム(株)技術開発センター Technical development center, Mitsubishi Aluminum Co., Ltd.
    • 当摩 建 TOHMA Ken
    • 三菱アルミニウム(株)技術開発センター Technical development center, Mitsubishi Aluminum Co., Ltd.

抄録

Electrochemical measurements as well as immersion corrosion tests were carried out in order to investigate the effect of Cu and Zn content in the filler on localized corrosion characteristics and corrosion rate of the filler, and on pitting corrosion resistance of Al–Mn brazing sheet. Both Cu and Zn segregated at eutectic α–phase of filler after brazing. Selective dissolution of eutectic α-phase occurred not only in Al–Si alloy filler but also in Al–Si–Zn and Al–Si–Cu alloys after brazing. In Al–9%Si–2%Zn alloy fillers containing more than 0.1%Cu, both inner primary α and eutectic α–phase of filler dissolved and the outer primary α undissolved. Dissolution characteristics of filler were closely related to the pitting potential difference between the phases depending on solid solubility of Si, Cu and Zn. Brazing sheet clad with the Zn containing filler can be pitting corrosion resistant, because corrosion rate of filler was not so high and the filler was effective as sacrificial anode for the core.

収録刊行物

  • 軽金属  

    軽金属 48(9), 465-470, 1998-09 

    The Japan Institute of Light Metals

参考文献:  14件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002665278
  • NII書誌ID(NCID)
    AN00069773
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    04515994
  • NDL 記事登録ID
    4572346
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-284
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ