- Effect of chemical composition on age-hardening behavior of 7003 aluminum alloys.
- 7003 アルミニウム ゴウキン ノ ジコウ コウカ キョドウ ニ オヨボス
この論文をさがす
抄録
The age-hardening behavior at various temperatures up to 453 K of the 7003 aluminum alloys with different compositions was studied by differential scanning calorimetry and transmission electron microscopy. The age-hardening behavior was affected by the amount of Zn and/or Mg contents. The incubation period of the age-hardening process became shorter and the peak hardness became higher with increasing the amount of Zn and/or Mg. The effects of Mg addition on the decreased incubation period and the increased peak hardness were greater by 2 to 7 times than those of Zn addition, compared in a unit mol%. The increase in Mg content at constant Zn concentration in Al–Zn–Mg alloys results in the increased amount of metastable precipitates with higher density and finer size. The increased amount of Mg, therefore, is effective to increase the age-hardenability of Al–Zn–Mg alloys.
収録刊行物
-
- 軽金属
-
軽金属 48 (12), 597-602, 1998
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206337816320
-
- NII論文ID
- 10002665545
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK1MXis1Wgsw%3D%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 4629137
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可