Nucleation and growth of discontinuous precipitation cells in Mg-Al alloys.
-
- HORI Shigenori
- Teikyo University [Present: Osaka University]
-
- OKA Shigeru
- Student, School of Science and Engineering, Teikyo University [Present: Heiwa Spring Co, Ltd.]
-
- FURUSHIRO Norio
- Osaka University
Bibliographic Information
- Other Title
-
- Mg‐Al合金における不連続析出セルの生成および成長
- Mg-Al合金における不連続析出セルの生成および成長
- Mg-Al ゴウキン ニ オケル フレンゾク セキシュツ セル ノ セイセイ オヨビ セイチョウ
Search this article
Abstract
The discontinuous precipitation process of Mg–Al alloys during aging has been investigated by metallographic observation. In Mg–Al alloys, the initial stage of discontinuous precipitation cell formation had preferential precipitation and local instability of the grain boundary. With continued aging, the local migration of the original grain boundary rose into the adjacent grain. Consequently a solute depleted region was formed behind the advancing grain boundary. After a while, the preproposed S-mechanism required for the formation of double seam morphology appeared. The occurrence of both single seam and double seam morphologies were conformed at both aging temperatures lower and higher than Tm/2 (Tm: melting temperature). These facts do not coincide with Baumann's assumption that the highest dependence is on aging temperature. After the solution treatment, a Mg–9.5Al specimen was cold compressed by 3.2∼15.3%. The cold work prior to aging does introduce additional nucleation sites for general precipitation, with the age hardening somewhat accelerated. The fractional area of discontinuous precipitation cells was suppressed by the deformation twins, only onset of cell formation increased the rate.
Journal
-
- Journal of Japan Institute of Light Metals
-
Journal of Japan Institute of Light Metals 49 (1), 24-29, 1999
The Japan Institute of Light Metals
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001206336633984
-
- NII Article ID
- 10002665780
-
- NII Book ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK1MXnt1ekuw%3D%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL BIB ID
- 3087517
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed