各種アルミニウム合金管とＳＵＳ３０４ステンレス鋼管の摩擦圧接性

• 川井 五作

  大阪産業大学工学部

• 小川 恒一

  大阪府立大学総合科学部

• 越智 秀

  大阪工業大学共同研究センター

• 時末 光

  日本大学生産工学部

書誌事項

タイトル別名

• Friction weldability of various aluminum alloy pipe to SUS304 stainless steel pipe.
• カクシュ アルミニウム ゴウキンカン ト SUS304 ステンレス コウカン ノ マサツ アッセツセイ

抄録

Friction welding of various aluminum alloy pipes to SUS304 stainless steel pipe was carried out making clear weldability at dissimilar material pipe. A1050/SUS304, A5052/SUS304, A5056/SUS304, A6061/SUS304 and A6063/SUS304 joints showed good weldability and the maximum joint efficiencies of these joints in tensile test were about 91%, 71%, 60%, 79% and 97%, respectively. In these cases, the formation of Al₁₃Fe₄ intermetallic compound was induced by the interdiffusion through the weld interface. On the other hand, other joints had poor weldability. In the cases of A2011/SUS304, A2017/SUS304 and A2024/SUS304 joints, CuAl₂ and Al₇Cu₂Fe were observed on the friction surface, and the maximum joint efficiencies of these joints were about 26%, 39% and 32%, respectively. For the case of A7075/SUS304 joint, Al₂₃CuFe₄ was observed on the friction surface, and the maximum joint efficiency was about 37%.

収録刊行物

• 軽金属

  軽金属 49 (2), 83-88, 1999

  一般社団法人 軽金属学会

キーワード

• friction welding
• dissimilar material
• intermetallic compound
• aluminum alloy
• SUS304 stainless steel
• pipe joint

詳細情報

• CRID: 1390001206337385472
• NII論文ID: 10002665899
• NII論文ID: 10004013965
• NII書誌ID: AN00069773
• DOI: 10.2464/jilm.49.83
• COI: 1:CAS:528:DyaK1MXhslGru7g%3D
• ISSN: 18808018
• ISSN: 04515994
• ISSN: http://id.crossref.org/issn/04515994
• NDL書誌ID: 4662061
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4662061
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可