一方向配向ラメラ組織を有する多結晶TiAl基合金の強度異方性 Anisotropic strength in a TiAl base polycrystal with unidirectionally oriented Iamellae

この論文にアクセスする

この論文をさがす

著者

抄録

A Ti–44.1 at%Al–1.6 at%Mn alloy with unidirectionally oriented lamellar structure was made by using heavy extrusion of a mixture of titanium and Al–Mn alloy powder followed by reactive sintering under HIP. Compression tests were performed for 5 × 5 × 6 mm samples prepared in such a way that angle between the extrusion direction and compression one becomes 0°, 30°, 45°, 60° or 90°. The yield strength at 293 K is found to strongly depend on the above angle, i.e., the 0° sample shows the highest strength, the 90° sample the second while the other samples show much lower strengths. A similar anisotropic yield strength is observed for the results obtained at 1073 K although the strength of the 0° sample is much higher than that of the 90° one. Anisotropic deformation behavior observed in the present investigation is discussed in comparison with that for TiAl PST crystals reported by Fujiwara et al..

収録刊行物

  • 軽金属

    軽金属 49(7), 282-286, 1999-07-30

    The Japan Institute of Light Metals

参考文献:  9件中 1-9件 を表示

  • <no title>

    KIM Y. W.

    J. Metals 43, 40, 1991

    被引用文献2件

  • <no title>

    FUJIWARA T.

    Phil. Mag. A 61, 591, 1990

    被引用文献4件

  • <no title>

    INUI H.

    Acta mater. 40, 3095, 1992

    被引用文献1件

  • <no title>

    JOHNSON D. R.

    Acta mater. 44, 2523, 1996

    被引用文献4件

  • 反応焼結法によるTiAlの製造

    渋江 和久

    住友軽金属技報 33(2), p98-104, 1992-04

    被引用文献1件

  • <no title>

    友田陽

    日本金属学会誌 60, 1007, 1996

    被引用文献1件

  • <no title>

    SUZUKI T.

    Phil. Mag. Letters 75, 337, 1997

    被引用文献1件

  • <no title>

    INUI H.

    Phil. Mag. A. 72, 1609, 1995

    被引用文献2件

  • <no title>

    INUI H.

    Phil. Mag. A 67, 1315, 1993

    被引用文献3件

各種コード

  • NII論文ID(NAID)
    10002666584
  • NII書誌ID(NCID)
    AN00069773
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    04515994
  • NDL 記事登録ID
    4807867
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-284
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ