５０８３アルミニウム合金の広い温度およびひずみ速度範囲にわたる超塑性と破面形態

DOI Web Site 被引用文献2件 参考文献36件

書誌事項

タイトル別名
  • Superplasticity and fractography over wide ranges of temperature and strain rate in a 5083 aluminum alloy.
  • 5083 アルミニウム ゴウキン ノ ヒロイ オンド オヨビ ヒズミ ソクド ハンイ ニ ワタル チョウソセイ ト ハメン ケイタイ

この論文をさがす

抄録

Superplasticity over the wide ranges of both temperature and strain rate has been investigated for a 5083 aluminum-magnesium base alloy. Large elongations of more than 300% were obtained in a temperature range of over 200 K and in a strain-rate range of the two orders of magnitude. Such large elongations were attributed to both grain boundary sliding and solute-drag controlled creep mechanisms. Fractography has been performed systematically in the light of deformation mechanism and elongation to failure. In a low strain rate, granular feature was observed on fracture surfaces. The granular feature was coarsened with increasing temperature. As temperature approached to an apparent solidus, fracture surface was accompanied with typical filaments suggesting the presence of a liquid phase. Near the apparent solidus temperature, a small amount of filaments was found at a strain rate of 1.4 × 10−2 s−1, while distinct intergranular fracture was found at 2.8 × 10−1 s−1. Consequently, it is reconfirmed that the morphology of fracture surface is correspondent with deformation mechanisms and elongation to failure.

収録刊行物

  • 軽金属

    軽金属 49 (8), 378-382, 1999

    一般社団法人 軽金属学会

被引用文献 (2)*注記

もっと見る

参考文献 (36)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ