Phase Transformations of C70 Fullerite under High Pressure of 6.5-12.5 GPa and Temperature 300-1830K:Comparison with C60
-
- Blank V. D.
- Research Center for Superhard Materials, 7a Centralnaya St.
-
- Buga S. G.
- Research Center for Superhard Materials, 7a Centralnaya St.
-
- Serebryanaya N. R.
- Research Center for Superhard Materials, 7a Centralnaya St.
-
- Dubitsky G. A.
- Research Center for Superhard Materials, 7a Centralnaya St.
-
- Sulyanov S. N.
- Shubnikov Institute of Crystallography RAS
書誌事項
- タイトル別名
-
- Phase Transformations of C70 Fullerite under High Pressure of 6.5-12.5GPa and Temperature 300-1720K: Comparison with C60.
- Phase Transformations of C70 Fullerite
この論文をさがす
抄録
High-pressure high-temperature polymerization of C70 fullerite obtained at first time. New crystal structures of rhombohedrally distorted fcc type and bct type are found for the samples quenched after treatment at p = 6. 5-12. 5 GPa and T = 500-900 K. In the temperature range of 900-1720 K a disordered cross-linked layered structures are found. Samples with bct type crystal structure and with disordered structure have hardness in the range of 30-90 GPa and their density varies in the range of 2. 1-2. 8 GPa. These data are compared with the data for materials obtained from C60 fullerite under the same conditions.
収録刊行物
-
- 高圧力の科学と技術
-
高圧力の科学と技術 7 814-816, 1998
日本高圧力学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679359233280
-
- NII論文ID
- 10002691929
-
- NII書誌ID
- AN10452913
-
- ISSN
- 13481940
- 0917639X
-
- NDL書誌ID
- 4494066
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可