- Matsumuro A.
- Department of Micro System Engineering, Nagoya University
-
- Takada Y.
- Department of Micro System Engineering, Nagoya University
-
- Takahashi Y.
- Department of Mechanical Engineering, Mie University
-
- Kondo I.
- Department of Mechanical Engineering, Daido Institute of Technology
-
- Senoo M.
- Department of Mechanical Engineering, Mie University
書誌事項
- タイトル別名
-
- Mechanical Properties of C60 Bulk Mater
この論文をさがす
抄録
Uniform bulk material of the polymerized C60 phase was synthesized under high-pressure sintering at 5. 4 GPa and 400°C for 2 h, and a bulk sample of the pristine phase was also obtained after subsequent heat treatment in a vacuum at 400°C for 2 h. The crystal structure of the polymerized bulk sample was iduntified as a fcc structure . Mechanical properties such as elastic moduli, hardness, compressive strength, frictional coefficients and wear rate were clarified Mechanical properties of the polymerized sample were higher markedly than those of the pristine phase due to intermolecular covalent bonds.
収録刊行物
-
- 高圧力の科学と技術
-
高圧力の科学と技術 7 823-825, 1998
日本高圧力学会
- Tweet
詳細情報
-
- CRID
- 1390001204382526592
-
- NII論文ID
- 10002691975
-
- NII書誌ID
- AN10452913
-
- ISSN
- 13481940
- 0917639X
-
- NDL書誌ID
- 4494069
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可