- High Pressure Sintering Behavior of B6O
この論文をさがす
抄録
Super-hard sintered composites in the systems of B6O-B4C and B6O-cBN were prepared by high pressure sintering of composite powders containing in-laboratory synthesized B6O powder. Nearly fully dense sintered composites were obtained under the high pressure and temperature treatment conditions of 3-6 GPa, 1500-1800°C and 10-30 min. Vickers microhardness of the sintered composites ranged form 3000 to 4600 kg/mm2 depending on the composition and sintering conditions. The fracture toughness of the B6O-cBN system which was higher than that of the B6O-B4C system, was observed by the enhanced crack propagation along the grain boundary between B6O and cBN.
収録刊行物
-
- 高圧力の科学と技術
-
高圧力の科学と技術 7 986-988, 1998
日本高圧力学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204382457600
-
- NII論文ID
- 10002692516
-
- NII書誌ID
- AN10452913
-
- ISSN
- 13481940
- 0917639X
-
- NDL書誌ID
- 4494121
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可