- Susaki Jun-ich
- Denka Research Center
-
- Suzuki Masaharu
- Denka Research Center
-
- Kikegawa Takumi
- PF, National Laboratory for High Energy Physics
-
- Shimomura Osamu
- PF, National Laboratory for High Energy Physics
書誌事項
- タイトル別名
-
- In-situ X-Ray Study of h-BN c-BN Phase
この論文をさがす
抄録
Phase relation among h-BN/w-BN/c-BN was observed using cubic anvil apparatus with synchrotron radiation. Starting material was pyrolytic hexagonal boron nitride (p-BN). Above 4. 5GPa, wurtzite phase (w-BN) reported to be stable above 10GPa was appeared at room temperature, while h-BN was unchanged. At temperature above 1000°C, diffraction peaks of c-BN was appeared at pressure higher than 7. 5GPa. Clear temperature dependence of the transition boundary from w-BN to c-BN was not observed. The transition boundary to c-BN lay between 7 . 1 and 7. 5 GPa with no temperature dependence up to 2000°C.
収録刊行物
-
- 高圧力の科学と技術
-
高圧力の科学と技術 7 995-997, 1998
日本高圧力学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679359169792
-
- NII論文ID
- 10002692551
-
- NII書誌ID
- AN10452913
-
- ISSN
- 13481940
- 0917639X
-
- NDL書誌ID
- 4494124
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可