Pressure Effect on Synthesis of TlSr_2Ca_2Cu_3O_y and TlSr_2Ca_3Cu_4O_y

この論文にアクセスする

この論文をさがす

著者

抄録

Thallium based cupurate superconductors, TlSr<SUB>2</SUB>Ca<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>y</SUB> and TlSr<SUB>2</SUB>Ca<SUB>3</SUB>Cu<SUB>4</SUB>O<SUB>y</SUB>, were synthesized using a high-pressure technique. Synthesis condition was 2. 5 GPa, 1000°C for 4 hours for TlSr<SUB>2</SUB>Ca<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>y</SUB>, and 1. 5 GPa, 950°C for 4 hours for TlSr<SUB>2</SUB>Ca<SUB>3</SUB>Cu<SUB>4</SUB>O<SUB>y</SUB>. Lattice parameters were α=3. 823 Å and c=15. 33 Å for TlSr<SUB>2</SUB>Ca<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>y</SUB>, and α=3. 830 Å and c=18. 49 Å for TlSr<SUB>2</SUB>Ca<SUB>3</SUB>Cu<SUB>4</SUB>O<SUB>y</SUB>. The synthesis pressure and heating time were fairly critical to obtain single phases. T<SUB>c</SUB> was 97 K and 90 K for TISr<SUB>2</SUB>Ca<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>y</SUB>, and TlSr<SUB>2</SUB>Ca<SUB>3</SUB>Cu<SUB>4</SUB>O<SUB>y</SUB>, respectively.

収録刊行物

  • 高圧力の科学と技術 = The Review of high pressure science and technology  

    高圧力の科学と技術 = The Review of high pressure science and technology 7, 1046-1048, 1998 

    The Japan Society of High Pressure Science and Technology

参考文献:  4件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002692764
  • NII書誌ID(NCID)
    AN10452913
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    0917639X
  • NDL 記事登録ID
    4494142
  • NDL 雑誌分類
    ZP1(科学技術--化学・化学工業)
  • NDL 請求記号
    Z17-1589
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ