- Improvement of wear resistance of aluminum alloy by plasma transferred arc welding process.
- プラズマ フンタイ ニクモリ ヨウセツホウ ニ ヨル アルミニウム ゴウキン ノ タイマモウ トクセイ ノ カイゼン
この論文をさがす
抄録
The purpose of this study is to improve the hardness and wear resistance characteristics of the aluminum alloy using Plasma Transferred Arc process, called PTA process. The PTA process has been mainly applied to surface modification to steel products. It has some difficulties to apply this PTA process into aluminum products due to its low melting point and high thermal conductivity. It can be possible to make stable surface modification to aluminum alloy optimizing plasma current and powder supply. Niobium carbide powder was selected to obtain the optimum hardness and wear resistance during a series of experiments using PTA process. As the conclusions, sufficient hardness and wear resistances were archived at the surface modified layer by controlling niobium carbide composition to aluminum powder in the PTA deposit metal. Deposits which have no blowhole, crack and detachment from base metal were obtained in case of more than 60%NbC content of mixture ratio.
収録刊行物
-
- 軽金属
-
軽金属 49 (9), 432-437, 1999
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681313639680
-
- NII論文ID
- 10002763322
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK1MXmsV2hsbY%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 4858561
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可