スチレンの懸濁重合における往復動撹拌の粒径分布に及ぼす影響 Effect of Forward-Reverse Mixing Method on Particle Size Distribution in Suspension Polymerization of Styrene

この論文にアクセスする

この論文をさがす

著者

抄録

スチレンの懸濁重合が往復動撹拌方式を採用して実施された.実験では, 翼幅の異なる4種類の撹拌翼を使用し, 重合過程におけるポリマー滴径の経時変化や最終ポリマー粒子径分布に及ぼす影響を検討するとともに, 一方向撹拌方式の結果と比較した.<BR>往復動撹拌方式では, 一方向撹拌方式と比べてポリマー滴の合一が抑制され, 結果として小さく, かつ, 均一性の度合いが高いポリマー粒子が生成された.また, 往復動撹拌方式は, 粒径を広範囲に変化させることができた。

Suspension polymerization of styrene was performed with a forward-reverse mixing method. In the experiments, four kinds of impellers were used and it was investigated how this mixing method affected the transient size distributions of polymer droplets and the size distributions of final polymer particles. The results were compared with those obtained by conventional mixing methods.<BR>The forward-reverse mixing method was found to prevent the polymer droplets from coalescing and to produce polymer particles of the smaller and more uniform sizes than the conventional mixing methods.<BR>Moreover, the forward-reverse mixing method was able to change the particle size dramatically.

収録刊行物

  • 化学工学論文集  

    化学工学論文集 23(2), 230-236, 1997-03-10 

    The Society of Chemical Engineers, Japan

参考文献:  11件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10002767258
  • NII書誌ID(NCID)
    AN00037234
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    0386216X
  • NDL 記事登録ID
    4161083
  • NDL 雑誌分類
    ZP5(科学技術--化学・化学工業--化学工学)
  • NDL 請求記号
    Z17-725
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ