Synthesis of Cubic B-C-N under Static High Pressure and Temperature and its Characterization.
-
- Nakano Satoshi
- National Institute for Research in Inorganic Materials
Bibliographic Information
- Other Title
-
- 立方晶B‐C‐Nの静的高温高圧合成とキャラクタリゼーション
- リッポウショウ B C N ノ セイテキ コウオン コウアツ ゴウセイ ト キ
Search this article
Abstract
Static direct transformation of graphitic BC2N to cubic forms was discussed on the basis of our results of synthetic experiments and characterizations for the products. The graphitic BC2N was successfully transformed to diamond-like cubic phases at 7. 7 GPa and 2150-2400°C for 15-60 min using a belt-type high-pressure apparatus. Crystallization of cubic B-C-N compound was confirmed in the products obtained at 2300°C by means of XRD and ATEM. The cubic B-C-N, however, was segregated to diamond and cBN with increasing the synthetic temperature to 2400°C, which was also supported by SEM and AES. The formation behavior seems to provide some conceptions to explore new materials by high-pressure synthesis.
Journal
-
- The Review of High Pressure Science and Technology
-
The Review of High Pressure Science and Technology 6 (4), 222-229, 1997
The Japan Society of High Pressure Science and Technology
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282679359074176
-
- NII Article ID
- 10002848838
- 10004195481
-
- NII Book ID
- AN10452913
-
- ISSN
- 13481940
- 0917639X
-
- NDL BIB ID
- 4367806
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed