• Mechanical alloying of high-carbon Fe-C alloy.
• コウ タンソ Fe C ゴウキン ノ メカニカル アロイング

抄録

Mechanical alloying (MA) of iron and graphite powders has been performed using a conventional ball-mill. MA process of Fe₁-xCx (x=0.17-0.90) powders has been studied by X-ray diffraction, transmission electron microscopy, scanning electron microscopy, 57Fe Mössbauer spectroscopy and differential scanning calorimetry.<BR>Results from X-ray diffraction and 57Fe Mbssbauer measurement suggest the formation of amorphous phase in powders ball-milled for about 200 hours. After subsequently long milling periods like 1000 hours, the formation of metastable carbides of Fe₃C and Fe₇C₃ has been detected for the powders of x=0.17-0.25 and x=0.29-0.70. Formation of super-paramagnetic Fe-C particles at room temperature has been detected by Mössbauer spectroscopy for the powders having a higher carbon content like x=0.90.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 37 (5), 660-664, 1990

  一般社団法人 粉体粉末冶金協会

キーワード

• Materials Chemistry
• Metals and Alloys
• Industrial and Manufacturing Engineering
• Mechanical Engineering

詳細情報

• CRID: 1390001206305878400
• NII論文ID: 130000813958
• NII論文ID: 10003343820
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.37.660
• COI: 1:CAS:528:DyaK3MXos1Wlug%3D%3D
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 3681804
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3681804
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可