Creep-induced Grain Boundary Damage and Creep Properties of SUS 304
-
- TANAKA Hideo
- National Research Institute for Metals
-
- MURATA Masaharu
- National Research Institute for Metals
-
- KAISE Masatsugu
- National Research Institute for Metals
-
- SHINYA Norio
- National Research Institute for Metals
Bibliographic Information
- Other Title
-
- SUS 304における粒界クリープ損傷とクリープ特性
- SUS304 ニ オケル リュウカイ クリープ ソンショウ ト クリープ トク
Search this article
Abstract
For the purpose of evaluating creep damage, systematic study of creep damage was performed, particularly for grain boundary creep damages by SEM observation and density change measurements. Three different kinds of grain boundary creep damages leading to creep fracture were observed. They are cracks formed at triple points at higher loading stress, grain boundary cavities at medium stress and cracks at sigma/austenite interface at lower stress. Both the grain boundary cavities and the cracks at sigma/austenite interface comence to form at comparatively low creep strain (0.1-0.6%) at the steady-state creep stage (t/tr:0.2-0.4).The increasing feature of cavity volume with creep time corresponds to the creep curves. Precipitation of AIN associated with sigma phase on grain boundary leads to early formation of the cracks at their interface. In this case, the volume of the cracks increases considerably in the accelerating creep stage and constitutes a main component of the creep strain. The rapid increase in the volume causes the transition from the steady-state to the accelerating creep stage.
Journal
-
- Tetsu-to-Hagane
-
Tetsu-to-Hagane 74 (10), 2009-2016, 1988
The Iron and Steel Institute of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282680127638144
-
- NII Article ID
- 110001492160
- 10003347857
-
- NII Book ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
- http://id.crossref.org/issn/00211575
-
- NDL BIB ID
- 3196630
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed