- 山下 治
- 住友特殊金属(株)研究開発部
書誌事項
- タイトル別名
-
- Magnetic Properties of Nd-Fe-B Magnets Prepared by Metal Injection Molding.
- キンゾク シャシュツ セイケイ デ サクセイシタ Nd Fe B ジシャク ノ
この論文をさがす
抄録
The Nd-Fe-B alloy powder was kneaded at 283K with the binder of methylcellulose dissolved in water. The mixture was injected at temperature 293K in a die of 353K, which is slightly above the sol-gel transformation temperature of methylcellulose. The magnetic field of 1.35 (MA/m) was applied to produce the alignment of easy magnetization direction of alloy powder in a molded body. The molded body was dehydrated by the vacuum-drying method to suppress the oxidation of alloy powder. By heating it in H2 at 573K for 0.5H, about 80% of carbon in binder was removed, although the oxygen in binder remained unremoved. With the molded body added 2wt% methylcellulose, these treatments can allow to suppress the residual contents of oxygen and carbon in the resulted sintered Nd-Fe-B alloy within less than 9000ppm and 800ppm, respectively. The highest coercive force (iHc) and maximum energy product (BH) m ?? x for a sintered anisotropic magnet prepared by the above mentioned process are 1.10(MA/m) and 287.2(kJ/m3), respectively.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 42 (9), 1073-1078, 1995
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681285683968
-
- NII論文ID
- 10001749818
- 10003380955
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3629450
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可