- HIP Sintering of the Fine Powder in the System ZrO2(3Y)-Al2O3.
- ZrO2 3Y Al2O3ケイ ビリュウシ フンタイ ノ HIP ショウケツ
この論文をさがす
抄録
The mixed powder of ZrO2(3Y) and Al2O3 was ground by a bead milling method. The particle sizes of ZrO2(3Y) and Al2O3 were reduced to 10 nm and 18 nm by milling for 377 hours, respectively. Open pores in the specimen sintered at 1300°C were diminished to less than 0.1% of total volume for fine mixed powder milled for 422 hr, while open pores in the specimen sintered at the same conditions using mixed powder milled for 1 hr showed more than 17%. Therefore, it was concluded that the reduction of particle size mentioned above greatly enhanced the sinterability of the mixed powder. The relative density reached more than 99.7% of theoretical density when the pre-sintered bodies free from open pores were HIP'ed at temperatures from 1300°C to 1500°C under Ar gas pressure of 196 MPa. The bending strength of the HIP'ed specimen was 1520 MPa although that of pre-sintered specimen was 800 MPa.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 39 (12), 1072-1075, 1992
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681283332224
-
- NII論文ID
- 130000818083
- 10003381014
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3791410
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可