高炭素高速度鋼の炭化物形成に及ぼすバナジウム添加の影響

• 宮坂 善和

  （株）淀川製鋼所鋳造部

• 江南 和幸

  龍谷大学理工学部　工博

• 谷川 俊宏

  同大学理工学部　学生

書誌事項

タイトル別名

• Effects of Vanadium Addition on Formation of Carbides of High Carbon High Speed Steel
• コウ タンソ コウソクド コウ ノ タンカブツ ケイセイ ニ オヨボス バナジ

抄録

  The effects of vanadium, from 1 to 10 mass %, on the formation of carbides of as cast high carbon high speed steels containing 1.6 and 2.1mass%C were investigated by SEM, TEM and EDS analyses. In the 1%V steels, M₇C₃ and M₆C type eutectic carbides formed on the primary austenite boundary. In the 3%V steels, V-rich MC type eutectic carbide was found to exist. In steels with V above 3% the amount of MC carbide increased while those of M₇C₃ and M₆C decreased with increasing V content. In both the 8% and 10%V steels, primary MC and eutectic M₃C carbides were observed. Carbon content influenced the start and finishing temperatures of the eutectic reaction and the microstructure, i. e. both the temperatures decreased and the length of needle-like eutectic carbides became longer in the 2.1%C steels. While the hardness of the steels with V below 5% did not change with V content, it began to drop suddenly in the steels with V above 8% due to the existence of ferritic matrix.

収録刊行物

• 鋳造工学

  鋳造工学 69 (3), 201-206, 1997

  公益社団法人 日本鋳造工学会

キーワード

• as cast
• high carbon high speed steel
• eutectic
• primary
• MC type carbide

詳細情報

• CRID: 1390001206507379200
• NII論文ID: 130004556273
• NII論文ID: 10003800010
• NII書誌ID: AN10514770
• DOI: 10.11279/jfes.69.201
• ISSN: 21855374
• ISSN: 13420429
• NDL書誌ID: 4172718
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I4172718
• 本文言語コード: en
• データソース種別:
  • JaLC
  • NDL
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可