燃焼合成法による球状黒鉛鋳鉄基板へのTi-Al系金属間化合物コーティング Ti-Al Intermetallics Coating on Spheroidal Graphite Cast Iron by Combusion Synthesis

この論文にアクセスする

この論文をさがす

著者

抄録

  A Ti-Al elemental powder mixture compact set on a spheroidal graphite cast iron have been hot pressed. Hot pressing made the compact combusion synthesized into Ti-Al intermetallics and simultaneously joined, and, as a result, the Ti-Al intermetallics were coated on the spheroidal graphite cast iron. The coating layer had malti-phases composed mainly of TiAl<sub>3</sub> and Ti solid solution, and had a little pore. Fe-Al layer, however, was formed at the coating layer / substrate interface.

収録刊行物

  • 鋳造工学 = Journal of Japan Foundry Engineering Society

    鋳造工学 = Journal of Japan Foundry Engineering Society 69(5), 403-407, 1997-05

    公益社団法人 日本鋳造工学会

参考文献:  6件中 1-6件 を表示

  • <no title>

    佐多

    金属 6, 7, 1989

    被引用文献2件

  • <no title>

    小泉

    燃焼合成研究会, 1992

    被引用文献2件

  • <no title>

    池永

    鋳造工学 68, 417, 1996

    被引用文献3件

  • <no title>

    池永

    鋳造工学 68, 852, 1996

    被引用文献1件

  • <no title>

    池永

    鋳造工学 69, 107, 1997

    被引用文献1件

  • <no title>

    MASSALSKI T. B.

    Binary Alloy Phase Diagrams 1, 175, 1986

    被引用文献2件

各種コード

  • NII論文ID(NAID)
    10003800284
  • NII書誌ID(NCID)
    AN10514770
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    13420429
  • NDL 記事登録ID
    4217020
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-277
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ