- Age-Hardening Behavior of Al-Si-Cu Base Cast Alloys
- Al-Si-Cuケイ チュウゾウ ゴウキン ノ ジコウ コウカ キョドウ
この論文をさがす
抄録
Age-hardening processes were investigated on pure Al-Si-Cu and Al-Si-Cu-Mg alloys containing about 7mass%Si, 2.72 to 4.08mass% Cu and 0 to 0.47mass%Mg and also on a commercial JIS-AC4B alloy by using a TEM, Vickers macro hardness tester and EPMA. A series of alloy specimens were solution treated at 773K for 10h, and subsequently aged at 433K and 473K for 10min to 104min. The typical hardness-aging time relations are obtained for each alloy specimen. Age-hardnening occurs faster in the Al-Si-Cu-Mg and AC4B alloys than in the ternary Al-Si-Cu alloy. The maximum hardness of the specimen aged at 433K increases from HV95 to HV152 as the Mg content of the alloy increases from 0 to 0.43mass%. TEM shows the high density dislocations distributing around the eutectic Si particles which are expected to have formed in the α phase during quenching from the solution-treatement temperature, because of the difference in the coefficient of thermal expansion between the α matrix and eutectic Si. The formation of the GP Zone is suppressed and the precipitation of θ’ is promoted in the ternary Al-Si-Cu alloy which contains higher density dislocations. A number of tiny particles of the Mn-rich compound precipitate in the α matrix of the solution-treated AC4B alloy, which decreases the Cu content of the α phase and the age-hardening ability of the AC4B alloy.
収録刊行物
-
- 鋳造工学
-
鋳造工学 69 (10), 828-834, 1997
公益社団法人 日本鋳造工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681483341568
-
- NII論文ID
- 130004556248
- 10003801158
-
- NII書誌ID
- AN10514770
-
- ISSN
- 21855374
- 13420429
-
- NDL書誌ID
- 4324268
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可