Wettability of Zirconia and Alumina Ceramics by Molten Zinc
-
- Shinozaki Nobuya
- Department of Materials Science, Faculty of Engineering, Kyushu Institute of Technology
-
- Suenaga Masami
- Department of Materials Science, Faculty of Engineering, Kyushu Institute of Technology
-
- Mukai Kusuhiro
- Department of Materials Science, Faculty of Engineering, Kyushu Institute of Technology
Search this article
Abstract
A basic research study for improvement of the galvanizing process has been conducted. The contact angle and surface tension of the molten zinc/oxide ceramic systems were measured at 873 and 973 K by the sessile drop method. The measurement became possible by using sponge titanium as deoxidizer under vacuum. It was found that zinc didn’t react or wet zirconia and alumina significantly. The surface tension of molten zinc decreased slightly with increasing temperature. On the basis of the work of adhesion, it was presumed that the dispersion force was predominant for the bond at zinc/zirconia and zinc/alumina interface.
Journal
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 40 (1), 52-56, 1999
The Japan Institute of Metals
- Tweet
Details 詳細情報について
-
- CRID
- 1390001204248625920
-
- NII Article ID
- 130003557098
- 10003805317
-
- NII Book ID
- AA10699969
-
- COI
- 1:CAS:528:DyaK1MXhvVWjtr0%3D
-
- ISSN
- 2432471X
- 09161821
-
- NDL BIB ID
- 4636087
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed