- Preparatin of BPSCCO superconductivity thick films by using of gas-depositin method and their properties.
- ガス デポジションホウ ニ ヨル BPSCCOケイ チョウデンドウ アツマク
この論文をさがす
抄録
Superconducting thick film of BPSCCO is formed on MgO substrate by gas deposition using fine powder of Oi-Pb-Sr-Ca-Cu-O(BPSCCO) having diameter less than 1μm. The pattern of the deposited film is linear, and the thickness of it can be controlled in the range of 5-200μm.<BR>After heat treatment at 770°C for 10hr in air atmosphere, Tc(end) showed 105K and critical current density of 225A/cm2 are obtained at 77K in zero magnetic field.<BR>The structure of the surface of thick film by X-ray diffraction pattern, and composition ratio of Ui and Pb in film, were reported.<BR>Tape like BPSCCO thick film with width of 10mm was formed on substrate using similar method. Tape like thick film is expected to utilize as material of superconducting tape.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 37 (1), 94-98, 1990
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681281572992
-
- NII論文ID
- 130000813787
- 10004219509
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 3654024
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可