- Directionally solidified structures and crystal orientations of aluminum strips cast continuously with an open type, heated horizontal mold.
- ジョウメン カイホウ カネツ イガタシキ レンゾク チュウゾウホウ ニ ヨル アルミニウムバン ノ 1ホウコウ ギョウコ ソシキ ト ケッショウ ホウイ
この論文をさがす
抄録
Cast 99.7 mass% aluminum strips were produced using the open type, heated mold continuous casting (Ohno Strip Casting) process at casting speeds of 1.7, 5.0 and 8.3 mm/s. The effects of casting speed on the solidified structures and crystal orientations of the strips were investigated. All strips were constituted macroscopically of unidirectionally solidified structures and microscopically of aligned primary and secondary cell grains extending parallel to the casting direction. At the starting end, the crystal orientation of the strip parallel to the casting direction was distributed from [001] to [011]. At 1400 mm away from the starting end, particularly at slow casting speed (1.7 mm/s), the crystal orientations of the strip tended to be [001], It was found that all primary cell grains had mixed boundary which consisted of tilt and twist angles. As the casting speed of the strips increased, tilt and twist angles of the primary cell grains increased. Higher casting speed also resulted in primary cell grain growth parallel to the casting direction with some slight twisting.
収録刊行物
-
- 軽金属
-
軽金属 49 (11), 542-547, 1999
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681314613632
-
- NII論文ID
- 10004453595
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK1MXnsF2rtrs%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 4917263
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可