Electrochemical Properties of Spherical,Porous LiMn2-xMgxO4 Powders Prepared by Ultrasonic Spray Pyrolysis
-
- OGIHARA Takashi
- Department of Materials Science and Engineering, Fukui University
-
- OGATA Nobuo
- Department of Materials Science and Engineering, Fukui University
-
- KATAYAMA Keiichi
- Faculty of Engineering, Tokai University
-
- AZUMA Yasuo
- Faculty of Engineering, Tokai University
-
- MIZUTANI Nobuyasu
- Department of Inorganic Materials, Faculty of Engineering, Tokyo Institute of Technology
書誌事項
- タイトル別名
-
- Electrochemical Properties of Spherical, Porous LiMn<sub>2−</sub><i><sub>x</sub></i>Mg<i><sub>x</sub></i>O<sub>4</sub> Powders Prepared by Ultrasonic Spray Pyrolysis
この論文をさがす
抄録
<p>Spherical LiMn2−xMgxO4 powders were prepared by the ultrasonic spray pyrolysis. As-prepared particles had a porous microstructure and were nonagglomerated, which had an average diameter of about 1 µm with narrow size distribution. XRD showed that as-prepared powders were well crystallized to spinel structure with Fd3m space group. ICP analysis revealed that Mg ions were homogeneously doped to LiMn2O4. As-prepared powders were used as cathode active material for lithium secondary battery and its electrochemical properties were investigated between 3.5 and 4.3 V. The first charge/discharge capacity of LiMn2O4 was 145 and 141 mAh g−1 at 0.1 mA cm−2, respectively. The discharge capacity of LiMn2O4 decreased with increasing cycle number. The first charge/discharge capacity of LiMn2−xMgxO4 was less than that of LiMn2O4. However, the cycle performance of LiMn2−xMgxO4 was superior to that of LiMn2O4.</p>
収録刊行物
-
- Electrochemistry
-
Electrochemistry 68 (3), 162-166, 2000-03-05
公益社団法人 電気化学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001277391401984
-
- NII論文ID
- 10004455026
-
- NII書誌ID
- AN00151637
-
- ISSN
- 21862451
- 13443542
- http://id.crossref.org/issn/13443542
-
- NDL書誌ID
- 5295392
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可