5052/2017アルミニウム合金摩擦圧接継手接合界面の機械的混合層と機械的性質 Mechanically mixed layer in weld interface and mechanical properties of friction welded 5052/2017 aluminum alloys joints

この論文にアクセスする

この論文をさがす

著者

抄録

The mechanically mixed layer at a weld interface and the mechanical properties of dissimilar welded joints of 5052 aluminum alloy to 2017 aluminum alloy, which were made by using a brake type friction welding machine were examined with different welding conditions. The mechanically mixed layer is formed on the friction process, and it is observed at a weld interface all over. The thickness of the mechanically mixed layer decreased with increasing friction pressure, the mixed layer of the outside of joint became thinner than that at the center. The tensile strength of joints which were made with the friction pressure of above 45 MPa, which had an average thickness of 200 μm in mechanically mixed layer, showed 85% of 5052 aluminum alloy base metal. The breakage occurred at the softened area of 5052 aluminum alloy side. The impact strength of joints, which had an average thickness of 200 μm in mechanically mixed layer, were 70% of 5052 aluminum alloy base metal.

収録刊行物

  • 軽金属  

    軽金属 50(4), 157-161, 2000-04-30 

    The Japan Institute of Light Metals

参考文献:  11件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  6件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10004548820
  • NII書誌ID(NCID)
    AN00069773
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    04515994
  • NDL 記事登録ID
    5362329
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-284
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ