TiN被覆ゴス珪素鋼板中に成長した単結晶の曲げ変形後のクラックの発生状況 Crack Morphology in Bend-forming of TiN-coated Single Crystal of Goss-Oriented Silicon Steel Sheet

この論文にアクセスする

この論文をさがす

著者

抄録

In order to clarify the crack morphology in 180° bend-forming of the TiN film deposited on (011) [100] single crystals of silicon steel, TiN coating by the hollow cathode discharge (HCD) method was done on a polished (011) [100] single crystal sample. The TiN-coated samples were 180° bend-formed and observed by the scanning electron microscope.<BR>In the position (a) just above 180° bend-forming, TiN film showed the straight crack at the interval of 2-4 μm parallel to the direction of [121] <SUB>TiN</SUB>. In contrast, in the position (b) near the transition zone from bend-forming to tensioning, TiN film showed an elliptical morphology 23-30 μm long and 9-12 μm wide.<BR>The point of origin of a small TiN crack can be seen near the center of the ellipse, and the straight crack in the TiN film will propagate from this origin.<BR>It should be noted that the TiN crack morphology differed remarkably depending on the positions of bend-forming.

収録刊行物

  • 真空  

    真空 43(7), 741-744, 2000-07-20 

    The Vacuum Society of Japan

参考文献:  7件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10004562606
  • NII書誌ID(NCID)
    AN00119871
  • 本文言語コード
    JPN
  • 資料種別
    SHO
  • ISSN
    05598516
  • NDL 記事登録ID
    5432356
  • NDL 雑誌分類
    ZN15(科学技術--機械工学・工業--流体機械)
  • NDL 請求記号
    Z16-474
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ