- The Precipitation Behavior of TiC and TiN on the Surface of SUS 304 and Fe Implanted with Ti<SUP>+</SUP>
- Ti+イオン注入したSUS304ステンレス鋼と純鉄におけるTiCとTiNの析出挙動
- Ti + イオン チュウニュウシタ SUS304 ステンレス コウ ト ジュン
この論文をさがす
抄録
SUS 304 stainless steel and Fe were implanted with 1×1017 Ti+/cm2 at room temperature. The surface composition of implanted SUS 304 and Fe at high temperatures was observed in vacuum with AES and XPS.<BR>The precipitation of Ti compounds was found on the surfaces of implanted SUS 304 and Fe. Implanted Ti+ into SUS 304 and Fe, which existed near the surfaces of metals, diffused into the inside of the surfaces and reacted on C and N in metals. At about 600 K, TiC precipitated on the surfaces of both SUS 304 and Fe. The precipitated TiC disappeared at about 1100 K and TiN precipitated on the surface of SUS 304, while on the surface of Fe this change was observed at about 750 K.<BR>The surface precipitation behavior is explained as follows: As TiN is thermodynamically more stable than TiC, the latter reacts on N which diffuses from the bulk of metal, and changes into TiN. The diffusion coefficient of N in Fe is larger than that of N in SUS 304. Therefore, the precipitation temperature of TiN on the surface of Fe is lower than on that of SUS 304.<BR>This precipitation behavior can be applied to the surface treatment of various metals.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 49 (11), 988-994, 1985
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報
-
- CRID
- 1390001206483616000
-
- NII論文ID
- 130007335807
- 10004659551
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 3058272
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可