Mixed Electronic-Oxide Ionic Conductivity and Oxygen Permeating Property in Ni Doped LaGaO_3 Perovskite Oxide
Access this Article
Search this Article
It was found that LaGaO<SUB>3</SUB> perovskite oxide doped with Ni for Ga site exhibits a high mixed electronic-oxide ionic conduction. Oxygen permeation rate was increased with increasing Ni content and it attained to a maximum value of 2.15 cm<SUP>3</SUP>/min cm<SUP>2</SUP> at 1273 K when 25 mol% Ni was doped.
- Chemistry Letters
Chemistry Letters 1999(12), 1257-1258, 1999-12-05