Mixed Electronic-Oxide Ionic Conductivity and Oxygen Permeating Property in Ni Doped LaGaO3 Perovskite Oxide
-
- Hiroshi Arikawa
- Department of Applied Chemistry, Faculty of Engineering, Oita UniversityDannoharu 700, Oita
-
- Takashi Yamada
- Department of Applied Chemistry, Faculty of Engineering, Oita UniversityDannoharu 700, Oita
-
- Tatsumi Ishihara
- Department of Applied Chemistry, Faculty of Engineering, Oita UniversityDannoharu 700, Oita
-
- Hiroyasu Nishiguchi
- Department of Applied Chemistry, Faculty of Engineering, Oita UniversityDannoharu 700, Oita
-
- Yusaku Takita
- Department of Applied Chemistry, Faculty of Engineering, Oita UniversityDannoharu 700, Oita
この論文をさがす
抄録
<jats:title>Abstract</jats:title> <jats:p>It was found that LaGaO3 perovskite oxide doped with Ni for Ga site exhibits a high mixed electronic-oxide ionic conduction. Oxygen permeation rate was increased with increasing Ni content and it attained to a maximum value of 2.15 cm3/min cm2 at 1273 K when 25 mol% Ni was doped.</jats:p>
収録刊行物
-
- Chemistry Letters
-
Chemistry Letters 28 (12), 1257-1258, 1999-12-01
Oxford University Press (OUP)
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1360846644039749120
-
- NII論文ID
- 10004703781
-
- NII書誌ID
- AA00603318
-
- ISSN
- 13480715
- 03667022
-
- データソース種別
-
- Crossref
- CiNii Articles