端部に高引裂材を用いた積層ゴム支承の圧縮下での静的および疲労せん断挙動 Static and Fatigue Shear Characteristics of Rubber-Metal Laminated Bearings Partially Using High Tearing Rubber at Their Edge under Compression

この論文にアクセスする

この論文をさがす

著者

抄録

The effect of the partial use of high tearing strength rubber at the edge of rubber-metal laminated bearings was examined. The static or cyclic fatigue shear loads were applied to the circular rubber bearing subjected to compressive load at room temperature. The specimens having a chambered edge at the laminating steel plates were also used.<br>The crack initiation was significantly delayed due to the use of high tearing strength rubber under static load, regardless of the edge shape of the steel plates and compressive load. For conventional rubber-metal laminated bearings fabricated by one kind of rubber, the edge shape affected the nominal shear strain at crack initiation in case of static low compression.<br>The shear modulus of the specimens with high tearing strength rubber under cyclic loading was slightly lower than that of conventional one. The visco-elastic tangential loss at 5Hz vibration was slightly decreased with an increase of the number of cyclic loading. This change was not related with the material and the magnitude of compressive load. The tangential loss for the specimen with high tearing strength rubber was larger than that of conventional one, and was affected by the compressive load at high frequencies (10Hz and 20Hz).

収録刊行物

  • 日本ゴム協會誌  

    日本ゴム協會誌 73(9), 511-517, 2000-09-15 

    THE SOCIRETY OF RUBBER SCIENCE AND TECHNOLOGYY, JAPAN

参考文献:  11件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10004751992
  • NII書誌ID(NCID)
    AN00189720
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    0029022X
  • NDL 記事登録ID
    5474731
  • NDL 雑誌分類
    ZP17(科学技術--化学・化学工業--高分子化学・高分子化学工業--ゴム・プラスチックス)
  • NDL 請求記号
    Z17-125
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ