Texture and Deformation Behaviour through Thickness Direction in Strip-cast 4.5wt% Si Steel Sheet.
-
- Park Jae Young
- School of Materials Science and Engineering, Seoul National University
-
- Oh Kyu Hwan
- School of Materials Science and Engineering, Seoul National University
-
- Ra Hyung Yong
- School of Materials Science and Engineering, Seoul National University
この論文をさがす
抄録
Fe–4.5wt%Si strips were made using vertical type twin-roll strip casting process, and the microstructure and texture of as-cast strips were studied through thickness direction. The heterogeneity of the texture and microstructure through thickness direction was observed. Between the subsurface layer and the middle layer, Goss texture, with the subgrains of low angle grain boundary was evolved by the shear deformation. In the center layer, major rolling and recrystallization textures with minor solidification texture were evolved.<br>The deformation behavior during strip casting process was simulated by hot rolling of Al alloy with temperature gradient through thickness direction. And the shear and normal strains distribution through thickness direction were measured. The heterogeneity of the texture and the microstructure through thickness direction resulted from the strength gradient, which originated from the temperature gradient through thickness direction.
収録刊行物
-
- ISIJ International
-
ISIJ International 40 (12), 1210-1215, 2000
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681430749056
-
- NII論文ID
- 10004837849
-
- NII書誌ID
- AA10680712
-
- COI
- 1:CAS:528:DC%2BD3MXoslWitg%3D%3D
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可