Microstructural and Mechanical Characteristics of Low Alloyed Ni-Mo-Cu Austempered Ductile Iron

この論文にアクセスする

この論文をさがす

著者

抄録

The present study investigated the effect of austempering temperature and austempering time on the microstructure and mechanical properties of low alloyed Ni–Mo–Cu ductile iron. The effect of austempering parameters and alloying additions on the austemperability of treated ductile iron has been estimated, too.<br>Specimens were austenitised at 900°C for 120 min, then austempered for 10, 30, 60, 120, 240 and 360 min at 300, 350 and 400°C respectively, and examined by light and scanning electron microscopy. The structure consisted of bainitic ferrite containing retained austenite, the amount of which increased, and the carbon content of which decreased, with increasing austempering temperature. The carbon content of austenite has been evaluated by measuring the lattice parameter by X-ray diffraction.<br>After short periods of austempering time in iron, the carbon content of the retained austenite decreases and on subsequent cooling to room temperature it transforms to martensite.<br>The volume fractions of retained austenite, bainitic ferrite, martensite and austenite carbon content was correlated with microstructural changes and mechanical properties. Optimum properties are obtained at intermediate austempering periods (120–240 min) when both the amount of retained austenite and austenite carbon content are maximum.

収録刊行物

  • ISIJ international

    ISIJ international 40(12), 1246-1252, 2000-12-15

    The Iron and Steel Institute of Japan

参考文献:  15件中 1-15件 を表示

  • <no title>

    VOIGHT R. C.

    Cast Metal 2, 71/93, 1989

    被引用文献1件

  • <no title>

    BLACKMORE P. A.

    Proc.1st Int.Conf.on Austempered Ductile Iron 117/134, 1984

    被引用文献1件

  • <no title>

    HARDING R. A.

    The Foundryman 86, 197, 1993

    被引用文献2件

  • <no title>

    GUNDLACH R. B.

    Met.Prog. 128, No.2, 19, 1985

    被引用文献1件

  • <no title>

    HARDING R. A.

    Foundry Trade Journal 4, 192, 1993

    被引用文献1件

  • <no title>

    RACE J.

    Heat Treatment of Metals 4, 105, 1991

    被引用文献1件

  • <no title>

    JANOWAK J. F.

    Trans.AFS 91, 377, 1983

    被引用文献1件

  • <no title>

    VOIGHT R. C.

    J.Heat Treat. 3, 291, 1984

    被引用文献1件

  • <no title>

    CULLITY B. D.

    Elements of X-ray Diffraction 350, 1978

    被引用文献2件

  • <no title>

    ROUNS T. N.

    Proc.Conf.on Transactions of the American Foundrymen's Society Vol.95, 851, 1987

    被引用文献1件

  • <no title>

    ROUNS T. N.

    Trans.AFS 92, 815, 1984

    被引用文献1件

  • <no title>

    VOIGHT R.

    Proc.1st Int.Conf.on Austempered Ductile Iron 83, 1984

    被引用文献1件

  • <no title>

    LEE Y. H.

    Trans.AFS 97, 915, 1989

    被引用文献1件

  • <no title>

    DARWISH N.

    Mater. Sci. Technol. 9, 572, 1993

    被引用文献3件

  • <no title>

    KOVACS B. V.

    Trans.AFS 102, 417-420, 1994

    被引用文献2件

各種コード

ページトップへ