Applicabilities of Equations of σm=ΨKicSmf1/2 and σd-1=σo-1+Ka1/2 to Soda Lime Glass
-
- Kawaguchi Yoshihiro
- Graduate Student in Course of Materials Science, The University of Tokyo
-
- Yanaba Yutaka
- Institute of Industrial Science, The University of Tokyo
-
- Hayashi Koji
- Institute of Industrial Science, The University of Tokyo
書誌事項
- タイトル別名
-
- Applicabilities of Equations of .SIGMA.m=.PSI.KICSmf1/2 and .SIGMA.d-1=.SIGMA.o-1+Ka1/2 to Soda Lime Glass.
- Applicabilities of Equations of シグマ m KicSmf1 2 and シグマ d 1 シグマ o 1 Ka1 2 to Soda Lime Glass
この論文をさがす
抄録
We have already clarified that our derived equations of σm=ΨKICSmf1/2 as well as σd-1=σo-1+Ka1/2 are applicable to various hard or brittle sintered materials such as WC-Co hardmetal and Si3N4 ceramics (σm: flexural strength, Ψ: shape factor, KIC: fracture toughness, Smf: total macroscopic fracture surface area of fragments, σd: external stress which operated on the fracture origin, σo: intrinsic or attainable fracture strength, K: material factor, a: half length of fracture origin). In this study, we investigated whether these two equations are applicable to soda lime glass which is non-crystalline and has extremely low KIC. It was found that both equations are also applicable to soda lime glass, when Smf+Sc is used in the application of the former equation, instead of Smf (Sc: the total macroscopic fracture surface area of internally stopped cracks). The fracture started from a visible microstructural defect with sizes of 10-30μm even for polished test pieces with σm values of 180-78 MPa. A correction was made in the derivation process of the former equation: the equation itself, however, was not changed.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 47 (3), 273-281, 2000
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206308162944
-
- NII論文ID
- 10005137322
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 5321008
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可