- Synthesis of TiB2-Ti(CN) Composites by Reactive Spark Plasma Sintering.
- ハンノウセイ ホウデン プラズマ ショウケツ ニ ヨル TiB2 Ti CN フクゴウタイ ノ ゴウセイ
この論文をさがす
抄録
Dense TiB2-TiCxN1-x and TiB2-Ti(C0.5N0.5)y composites were synthesized from powder mixtures of B4C, BN and Ti by reactive spark plasma sintering. The reaction 2xB4C+2(1-x)BN+3(x+1)Ti→(3x+1)TiB2+2TiCxN1-x for TiB2-TiCxN1-x and the reaction B4C+BN+(5/2+2/y)Ti→5/2TiB2+2/yTi(C0.5N0.5)y for TiB2-Ti(C0.5N0.5)y, proceeded during their sintering. The relative density of the TiB2-TiCxN1-x composites increased as the nitrogen content decreased, and the composites had relative densities more than 99 % at higher x than 0.5. The Young's modulus, Vickers hardness and fracture toughness of the composites increased with increasing x. For TiB2-Ti(C0.5N0.5)y composites, the relative density became still higher than 99.1 % at smaller y than 1, i.e., increasing nonstoichiometry. However, the Young's modulus, Vickers hardness and fracture toughness decreased with decreasing y value.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 47 (3), 308-314, 2000
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681284883456
-
- NII論文ID
- 10005137389
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD3cXivVSnu70%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 5321031
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可