- Production and Mechanical Properties of Zr-Based Metallic Glassy Wires.
- Zr キキンゾク ガラス センザイ ノ サクセイ ト キカイテキ セイシツ
この論文をさがす
抄録
Zr65Al7.5Cu27.5(Z-3), Zr65Al10Cu15Ni10(Z-4)and Zr55Al15Cu15Ni10Ti5(Z-5)glassy wires with a large supercooled liquid region were produced by a newly designed method, i. e., melt extraction using an arc furnace. The wire has a circular cross section and a smooth peripheral surface, but small flaws are observed on the surface. The Tg and Tx of the Z-4 and Z-5 glassy wires are nearly the same as those of the melt-spun glassy ribbons. The Z-4 glassy wire has a large super coold liquid region of 95 K. The coefficient of thermal expansion of the Z-4 glassy wire is 9.2 × 10-6K-1 and the temperature of electrical resistance of the Z-5 glassy wire is-9.0×10-5 K-1, respectively. Tensile fracture strength and elongation are 1170 MPa and 1.9 %, respectively, for the Z-3 glassy wire and 1590 MPa and 2.2 %, respectively, for the Z-4 glassy wire. The fracture surface consists mainly of a vein pattern which is the same as that for amorphous alloys.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 47 (4), 427-432, 2000
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681284418176
-
- NII論文ID
- 10005137658
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 5362825
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可