磁性材料　　小粒径針状α‐ＦｅＯＯＨから作製した配向性Ｍｎ‐Ｚｎフェライトの磁気特性

• 寺澤 誠

  埼玉大学大学院理工学研究科

• 柿崎 浩一

  埼玉大学大学院理工学研究科

• 平塚 信之

  埼玉大学大学院理工学研究科

書誌事項

タイトル別名

• Magnetic Properties of Crystal-Oriented Mn-Zn Ferrites Made from Small Size .ALPHA.-FeOOH Particles.
• ショウリュウケイシンジョウ アルファ FeOOH カラ サクセイ シタ ハイコウセイ Mn Zn フェライト ノ ジキ トクセイ

抄録

Acicular manganese zinc ferrite fine particles were made from small acicular α-FeOOH, Mn(C₅H₇O₂)₃, and Zn(C₅H₇O₂)₂. The long axis of these fine particles was oriented in parallel to the external magnetic field of 557kA/m, and then formed into multi-layered toroidal core. The green compact was sintered at 1200°C for 6 hours in air, and then cooled in a nitrogen atmosphere. The relative bulk density of the sintering body was improved from 87.0% to 90.2%. Crystallites consisted of the {110} plane were aligned along the upper plane of toroidal core of crystal-oriented manganese zinc ferrite. The initial permeability of crystal-oriented manganese zinc ferrite was 2240 at 0.1 MHz. The sample exhibited excellent high frequency magnetic properties.

収録刊行物

• 粉体および粉末冶金

  粉体および粉末冶金 47 (7), 752-756, 2000

  一般社団法人 粉体粉末冶金協会

キーワード

• small acicular particle
• crystal-oriented manganese zinc ferrite
• initial permeability
• tanδ

詳細情報

• CRID: 1390282681284121600
• NII論文ID: 10005138169
• NII書誌ID: AN00222724
• DOI: 10.2497/jjspm.47.752
• ISSN: 18809014
• ISSN: 05328799
• NDL書誌ID: 5410229
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I5410229
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可