- Geometrical Defect of Soft-Magnetic Material and Its Magnetic Restoration by Ferromagnetic Powder.
- ソフト ジセイ ザイリョウ ノ ザイリョウ ケッカン ト キョウジセイ フンマツ ニ ヨル シュウフク コウカ
この論文をさがす
抄録
The objective of this study is firstly to elucidate the effect of geometrical defect (artificial semi/full slit) on magnetic properties and secondly to evaluate the magnetic restoration by ferromagnetic paste filling to slit for the 4-types of soft magnetic materials. In this case, ferromagnetic pastes consist of the mixture of water-atomized powder of almost the same type (as specimen) and binding agent.<BR>The results obtained were summarized as follows:<BR>(1) DC magnetic properties are more or less degraded by semi/full slit, where magnetic induction (B) are less degraded in comparison with maximum permeability (μm), especially for high-μ permalloy.<BR>(2) AC magnetic properties, especially, specific permeability (μa) are degraded nearly in the same way as DC ones in low frequency range and less degraded at higher frequency (degradation ratio Δμa/μa<0.1, 100kHz).<BR>(3) As for DC magnetic properties, magnetic induction (B) tends to be more restored than maximum permeability (μm) by ferromagnetic paste filling to slit, although fairly plot-scattered.<BR>(4) AC magnetic properties at 60Hz also are enhanced upto restoration ratio Δμa'/Δμa-1/2 roughly by ferromagnetic paste filling to full slit, almost irrespectively of material type and slit width.<BR>(5) This ferromagnetic paste method is more effective in DC or low frequency range due to the result that Δμa/μa is fixed small for semi slit and linearly decreases for full slit with rise of applied frequency.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 46 (6), 659-665, 1999
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報
-
- CRID
- 1390282681286141184
-
- NII論文ID
- 10005139680
- 10005139694
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 4770288
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可