乾湿繰り返し環境における低合金鋼の腐食挙動に与えるタングステンの影響

書誌事項

タイトル別名
  • Effect of W on Corrosion Behavior of Low Alloy Steel in Wet/dry Environment
  • カンシツ クリカエシ カンキョウ ニ オケル テイゴウキン コウ ノ フショク キョドウ ニ アタエル タングステン ノ エイキョウ

この論文をさがす

抄録

The chemical state of the tungsten (W) in the rust of low alloy steel was analyzed by EPMA and XPS, and the electrochemical behavior of rust was investigated by alternating current (AC) impedance method after wet/dry cyclic corrosion test with chlorides. The 1.0mass%W-bearing steel showed higher corrosion resistance than carbon steel in the corrosion test. EPMA and XPS showed that the tungsten existed as WO4 compounds in the rust of W-bearing steel. A Fe-W binary potential-pH diagram was made to investigate the thermodynamic stability of Fe-W oxides, and this showed that WO4 was stable in the rust, which confirmed the physical analysis. An AC impedance measurement was made to obtain the corrosion reaction resistance (Rt) of the rust, and it was found that Rt of W-bearing steel was much larger than that of carbon steel. The corrosion of the W-bearing steel is suppressed by (1) the insoluble FeWO4 formed near the base metal suppressing the anodic reaction, (2) the WO42- ions in the rust changing the selective permeability to prevent the transport of Cl- ions.

収録刊行物

被引用文献 (3)*注記

もっと見る

参考文献 (16)*注記

もっと見る

詳細情報

問題の指摘

ページトップへ