素粉末混合法によるO相基Ti-22Al-27Nb合金の製造とその機械的性質

DOI Web Site Web Site 被引用文献1件 参考文献15件

書誌事項

タイトル別名
  • Blended Elemental P/M Synthesis and Property Evaluation of an Orthorhombic Ti-22Al-27Nb Alloy
  • ソ フンマツ コンゴウホウ ニ ヨル Oソウキ Ti-22Al-27Nb ゴウキン ノ セイゾウ ト ソノ キカイテキ セイシツ

この論文をさがす

抄録

The orthorhombic (O) phase based on the compound Ti2AlNb(Ti-25Al-25Nb(mol%)) has a higher strength-to-density ratio and better room temperature ductility than conventional titanium aluminides such as TiAl and Ti3Al. In the present study, orthorhombic Ti-22Al-27Nb alloy was produced by the blended elemental (BE) powder metallurgy (P/M) method, and the microstructures and mechanical properties such as tensile and high cycle fatigue were evaluated.<BR>Homogeneous BE P/M Ti-22Al-27Nb was successfully produced by using extra low chlorine Ti powder and Al-Nb master alloy powder with a particle size smaller than 45 μm. The microstructure in the as-HIP’ed condition consisted of O, α2 and β phases. The O and β phases were distributed in the interior of the grains whereas the α2 phase was mainly formed along the grain boundaries. The post-HIP heat treatment at 1173 K for 36 ks made the distribution of these three phases more homogeneous. Although the tensile specimen was broken before the peak tensile strength was attained in the temperature range up to 923 K, both 0.2% proof stress and fracture strength were higher than those for the Ti-6Al-2Sn-4Zr-2Mo alloy. The Young’s modulus and high cycle fatigue strength at 107 cycles in the as-HIP’ed condition were 129 GPa and 480 MPa, respectively. High cycle fatigue strength was increased to 540 MPa by the post-HIP heat treatment.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 63 (10), 1269-1276, 1999

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

参考文献 (15)*注記

もっと見る