Corrosion Behavior of Zr–(Nb–)Al–Ni–Cu Glassy Alloys

DOI Web Site Web Site 被引用文献12件 参考文献34件

書誌事項

タイトル別名
  • Corrosion Behavior of Zr–(Nb–)Al–Ni–Cu Glassy Alloys

この論文をさがす

抄録

The melt-spun glassy Zr60−xNbxAl10Ni10Cu20 (x=0, 5, 10, 15, 20 at%) alloys were found to exhibit a large supercooled liquid region (ΔTx) exceeding 42 K before crystallization. The largest ΔTx for the glassy alloys containing Nb reaches as large as 82 K for the Zr55Nb5Al10Ni10Cu20 alloy. The glass transition temperature (Tg) increases and the ΔTx value decreases with increasing Nb content. The corrosion behavior of the Zr–(Nb)–Al–Ni–Cu glassy alloys was examined by mass loss (=weight loss) and electrochemical measurements. In 1N HCl solution at 298 K, the addition of Nb for replacing some portion of Zr is effective in improving the corrosion resistance of the investigated Zr-based glassy alloys. The corrosion rate significantly decreases with increasing Nb content. The pitting potential and open circuit potential rise with Nb content. In 3%NaCl solution, the addition of Nb effectively increases the pitting potentials of the glassy alloys. In 1N H2SO4 solution, the corrosion rates of the glassy alloys are 10−4∼10−3 mm·y−1 (1 mm·y−1=0.317 pm·s−1). They are spontaneously passivated and have a wide passive region with significantly low passive current density. The open circuit potential increases with an increase in Nb content.

収録刊行物

被引用文献 (12)*注記

もっと見る

参考文献 (34)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ