Formation and Magnetic Properties of Bulk Glassy Fe–Co–Nd–Dy–B Alloys with High Boron Concentrations
-
- Zhang Wei
- Inoue Superliquid Glass Project, Exploratory Research for Advanced Technology, Japan Science and Technology Corporation
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Formation and Magnetic Properties of Bulk Glassy Fe–Co–Nd–Dy–B Alloys with High Boron Concentrations
この論文をさがす
抄録
New Fe-based glassy alloys in Fe–Co–Nd–Dy–B system with high boron concentrations were found to exhibit a wide supercooled liquid region exceeding 50 K. The high stability of the supercooled liquid enabled us to produce cylindrical bulk glassy alloys with diameters up to 0.75 mm by copper mold casting. The glass transition temperature (Tg), crystallization temperature (Tx), supercooled liquid region ΔTx (=Tx−Tg) and heat of crystallization of the φ0.75 mm rod of glassy Fe62Co9.5Nd3Dy0.5B25 alloy are 844 K, 899 K, 55 K and 4.46 kJ/mol, respectively. No appreciable difference in the thermal stability is seen between the bulk rods and melt-spun ribbon. The saturation magnetization (Is), coercive force (Hc), saturated magnetostriction (λs) and Curie temperature (Tc) of the melt-spun Fe62Co9.5Nd3Dy0.5B25 ribbon are 1.37 T, 4.58 A/m, 17.9×10−6 and 663 K, respectively, and Is and Tc are nearly the same as those for the bulk glass rods with diameters of 0.5 and 0.75 mm. The success of forming the Fe-based bulk glassy alloys exhibiting good soft magnetic properties is promising for future development as a new type of soft magnetic material.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 41 (12), 1679-1682, 2000
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679222736896
-
- NII論文ID
- 130003557355
- 10005354805
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DC%2BD3MXhtlWms7g%3D
-
- ISSN
- 2432471X
- 09161821
-
- NDL書誌ID
- 5883313
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可